Some mechanical properties of lanthanum metal
Loading...
Authors
Schuyler, Donald Richard
Issue Date
1962
Type
Thesis
Language
en_US
Keywords
metallurgy , melting , metal , fabrication , equipment , hardness , X-ray diffraction , recovery , recrystallization , lanthanum , Mackay Science Project
Alternative Title
Abstract
Recovery, recrystallization, hardness, and x-ray studies were made on a commercially produced lanthanum metal„ Arc melted lanthanum was cold worked and vacuum annealed to provide specimens for testing. Lanthanum of this purity was found to work harden rapidly and therefore fail with relatively low amounts of cold work. Definite recrystallization phenomena were not determined although recrystallization is postulated to start in the 40QOC region, with recovery starting at approximately 175° to 250°C.
Description
Online access for this thesis was created in part with support from the Institute of Museum and Library Services (IMLS) administered by the Nevada State Library, Archives and Public Records through the Library Services and Technology Act (LSTA). To obtain a high quality image or document please contact the DeLaMare Library at https://unr.libanswers.com/ or call: 775-784-6945.
Citation
Publisher
University of Nevada, Reno
License
In Copyright(All Rights Reserved)